Yield Strength | 46000 lbs/in² |
Tensile Strength | 98000 lbs/in² |
Elongation percent in 2 inches | 55 % |
Hardness (Rockwell B) | 86 |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 17000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 12000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 7000 lbs/in² |
Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 4000 lbs/in² |
Density | 0.29 lbs/in³ |
Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² |
Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs |
Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF |
Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.6 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.9 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.2 x 10-6 ºF |
Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.4 x 10-6 ºF |
Melting Point Range | 2550 to 2650 ºF |
Electrical Resistivity | 72 µΩ.cm |
Max. Operating Temp. (Continuous Service) | 1650 ºF |
Max. Operating Temp. (Intermittent Service) | 1500 ºF |
Welding Properties | Excellent |
Drawing and Stamping | Good |
Hot Working - Initial Forging | 2100 to 2300 ºF |
Annealing Temp. | 1850 to 2050 ºF |
Stress Relieving Temp. | 400 to 750 ºF |