Types 309 and 309S are austenitic chromium-nickel stainless steels that provide excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. Type 309S is identical to Type 309 except for a lower carbon content that minimizes carbide precipitation and improves weldability. They are essentially non-magnetic as annealed and become slightly magnetic when cold worked.

  Contact Now
Product Details

Types 309 and 309S are austenitic chromium-nickel stainless steels that provide excellent corrosion resistance and heat resistance plus good strength at room and elevated temperatures. Type 309S is identical to Type 309 except for a lower carbon content that minimizes carbide precipitation and improves weldability. They are essentially non-magnetic as annealed and become slightly magnetic when cold worked.

 

Typical uses include furnace parts, heating elements, aircraft and jet engine parts, heat exchangers, carburizing-annealing boxes, sulfite liquor handling equipment, kiln liners, boiler baffles, refinery and chemical processing equipment, and auto exhaust parts.

 pipe 325.jpeg

309 stainless steel can withstand repeated heating below 980 ℃, and has high high temperature strength, oxidation resistance and carburization resistance. It is widely used in boilers, energy (nuclear power, thermal power, fuel cells), industrial furnaces, incinerators, heating furnaces, chemical, petrochemical and other important fields.

 

Chemical Composition:

 

C≤0.08

Mn≤2.00

Si≤1.00

P≤0.045

S≤0.030

Ni≤12.0-15.0

Cr≤22.0-24.0

 

Mechanical Properties:

 

Yield strength/MPa: ≥ 205

Tensile strength/MPa: ≥515

Elongation/%: ≥ 40

Reduction of area/%: ≥50